Products Grade

1000
board 

1260
board

1400
board

1600
board 

Classification Temperature

°C 

1000 

1260 

1400 

1600 

    Max Use Temperature

°C 

850 

1100 

1200 

1400 

Chemical Composition

Al₂O₃ 

% 

40.1 

44 

52 

65 

SiO₂ 

% 

54.3 

54 

47 

34 

Density

kg/m³ 

250; 280; 300; 350; 400;

400 

Thermal Conductivity
W/(m. K) 

400 

°C 

(0.08) 

(0.09) 

(0.07) 

600 

°C 

(0.13) 

(0.14) 

(0.10) 

800 

°C 

(0.20) 

(0.18) 

(0.14) 

(0.17) 

1000 

°C 

(0.20) 

(0.21) 

1200 

°C 

(0.25) 

Linear Shrinkage  ( °Cx8H) 

% 

900°C 1.3 

1100°C 1.1 

1200°C  1.6 

1400°C 1.0 

Flexural  strength

kg/cm² 

5 

5 

5 

8 

Size  

mm 

1000 

blanket

1260 

blanket

1350 

blanket

1430 

blanket

1500 

blanket

1600 

blanket

°C 

1000 

1260 

1350 

1430 

1500 

1600 

°C 

900 

1100 

1200 

1250 

1300 

1580 

°C 

1760 

1760 

1760 

1760 

1760 

1760 

μm 

3.5 

2.8 

2.8 

2.8 

3.5 

3.1 

Fiber length

mm 

250 

250 

250 

250 

150 

100 

Shot content(>212μm)

% 

18 

18 

18 

18 

15 

0.11 

Chemical

Composition

Al₂O₃ 

% 

43 

46 

49 

35 

43 

72 

SiO₂ 

% 

53 

53.1 

44.2 

49.7 

53.4 

27.7 

ZrO₂ 

% 

- 

- 

6 

15 

- 

Cr₂O₃ 

% 

- 

- 

- 

- 

28 

- 

kg/m³ 

96;  128;  160 

Themal condustivity (W/m.K) 

DENSITY

128kg/m³

400 

°C 

(0.12) 

(0.07) 

(0.08) 

600 

°C 

(0.17) 

(0.12) 

(0.16) 

(0.13) 

(0.15) 

(0.13) 

800 

°C 

(0.25) 

(0.16) 

(0.20) 

(0.20) 

(0.20) 

(0.17) 

1000 

°C 

(0.27) 

(0.29) 

(0.27) 

(0.24) 

Linear shrinkage

( °Cx24H)

% 

1000°C < 
2.0 

1100°C< 
1.8 

1200°C< 
 2.5 

1300°C < 1.5 

1400°C< 
3.0 

1500°C< 
1.0 

L x W x T

mm 

7200x610x6 ; 7200x610x12.5; 7200x610x20; 7200x610x25; 3600x610x50;